Polymer Composite Diamond Coatings Specifications

Series 1000 
For Most Ferrous & Non-Ferrous Metals

Coating Specifications

Suitable Coating Materials

Polymer composite diamond coatings can be successfully integrated with most ferrous and non-ferrous metals: steel, stainless steel, iron, brass, bronze, copper, Hastelloy™, Inconel™, Monel™ and other nickel alloys, as well as aluminum and their alloys.

Composite Coating Thickness

The recommended composite coating thickness depends generally on the application and desired performance factors. The coating is a controlled process for diffusion-surface growth, and overall deposits are normally applied between 0.0005 and 0.003 inch. Based on the specific performance factors, dimensional growth may be as low as 0.0002 or as high as 0.010 inch.

Surface Finish (RMS)

Series 1000 Polymer Composite Diamond Coatings are conformal and are expected to provide a surface finish equal to the original surface finish; consequently, any surface imperfection before coating will remain after coating. Unique surface patterning is also attainable to create a variety of aesthetic or functional surface re-configurations.

Hardness

The 1000 series coatings exhibit the benefits of extreme wear with equivalent hardness of 90+ Rc, providing unsurpassed properties for friction, wear and surface energy.

Wear and Abrasion Resistance

The polymer diamond coating composites exhibit superior wear and shear strength not attained from pure ceramics, carbide, chromium or other hardened alloys. The diamond particulate provides one the best wear surfaces available for your difficult application.

Low Friction

Polymer Composite Diamond Coatings are conformal or geometrically enhanced surfaces to provide an extremely low coefficient of friction. Values are similar to Teflon® or other lubricants, typically ranging between 0.08 and 0.20, depending on vector load, sliding speed, mating surfaces, temperature and other factors. For optimal low friction, surfaces may require a nominal 12 RMS finish or better, before coating.

Chemical & Corrosion Resistance

Series 1000 Coatings are resistant to most chemicals, acids, alkali and solvents, exhibiting excellent corrosion resistance.  Endura® 1100-CR and 1100-S4 are engineered to provide maximum corrosion protection. Using a 5% salt spray test per ASTM B-117 and a coating thickness of 0.0012 inch, M1 coatings have shown to withstand corrosive attacks of 500 to 2000 hours. Upon request, we will supply coated samples and recommend your evaluation of selected coatings, under your specific application conditions.

Non-Stick Properties

Based on the combined unique properties of Polymer Composite diamond coatings, few materials will permanently adhere to the coated surface, providing a very good non stick coating option.

Operating Temperature Range

Coatings will withstand severe temperature extremes without loss in physical properties, and most are designed for operation typically from cryogenic to 500ºF for continuous operation.

Non-Wetting

Series 1000 Coatings are oleophobic and hydrophobic, resisting wetting by most liquids. Cleanup of your parts with the 100 series coating is easier, more thorough and, in many cases, reduced or unnecessary.